1. 石墨烯玻璃鳞片底漆 Graphite glass flake primer

石墨烯玻璃鳞片底漆 DreamCover 152 Gns: It is a two component, amine cured modified epoxy coating. It is a thick paste product with low surface treatment and high solid content. Because there are glass flakes to enhance, Improved its wear resistance and scratch resistance. Specially used in areas where ideal surface treatment cannot or is not required. It can provide long-term anti-corrosion protection in highly corrosive environments. It can be used as a primer, intermediate paint, topcoat, or single coat system in atmospheric and immersion environments. Suitable for properly treated carbon steel and aged painted surfaces. Construction can be carried out when the surface temperature is below 0 ℃

石墨烯玻璃鳞片底漆 Graphite glass flake primer is composed of epoxy resin, colorful pigments, wear-resistant filler, additives and solvents, and the other component is special curing agent of two component self-drying coating.

2. Quality of the surface treatment

石墨烯玻璃鳞片底漆 Graphite glass flake primer The surface of the equipment shall be strictly treated according to the (USA) Steel Structure Paint Committee SSPC (Steel Structures Painting Council, USA) or other equivalent standards, and the paint shall be properly selected and the coating process shall be carefully followed.

The quality of surface treatment must be strictly inspected, and shall not be painted without meeting the requirements of the standard.

石墨烯玻璃鳞片底漆 DreamCover 152 GnsPainting application shall comply with the requirements specified herein.

3.石墨烯玻璃鳞片底漆 Graphite glass flake primerEnvironmental restrictions

If the equipment is painted at the Contractor's plant, the Contractor must ensure that good surface cleaning, air dust free, good ventilation and lighting, and proper temperature and humidity conditions exist.

For materials conducted in the open air, 石墨烯玻璃鳞片底漆 DreamCover 152 Gns Work, do not paint in bad weather conditions, such as high humidity, windy weather. Unless appropriate measures are taken to overcome these difficulties.

During surface treatment and painting, the treated surface temperature is at least 3 C above the surrounding air dew point.

In hand石墨烯玻璃鳞片底漆 DreamCover 152 Gns During construction, the temperature of the treated surface shall not be lower than 7 C and not higher than 38 C.

Moisture and humidity limitation

石墨烯玻璃鳞片底漆 DreamCover 152 GnsDo not in the sun, exposure and rain, snow and fog;石墨烯玻璃鳞片底漆 DreamCover 152 GnsDo not apply paint in smoke or in relative humidity when paint condenses on the metal surface due to changes in metal temperature and ambient temperature.

Unless otherwise specified and recommended by the paint manufacturer, painting shall be performed at relative humidity lower than 85%.

All surfaces are under construction of石墨烯玻璃鳞片底漆 DreamCover 152 Gns shall be completely dry before and within 24 hours after painting.

Time slicing

Generally, the primer should be applied to the sandblasting treatment area within 4 hours after the completion of the sandblasting treatment. After this time, the surface should be treated for a second time. This time limit may be modified to more than 4 hours or less depending on the temperature and humidity control implemented. The main standard shall be no rust film on the surface before primer. If any rust coating is formed, the surface shall be sandblasted before priming.

The interval time of coating should be strictly controlled according to the coating process.

Temperature limitation

Unless otherwise specified and suggested by the paint manufacturer, in general, the 石墨烯玻璃鳞片底漆 DreamCover 152 Gns Painting shall be performed from 10℃ to 32℃. Paint should not be applied when the ambient air temperature is below 5℃ or when the temperature is expected to drop to 0℃ before the paint is dry.

Steel at temperatures above 50℃ shall not be painted unless specially prepared paint is applied at this temperature. When steel is painted in hot climate, precautions should be taken to ensure obtaining the required dry film thickness.

The welding part can only be painted after 72 hours of welding.

Construction can be carried out only when the substrate temperature is above 3℃ above the dew point. Do not paint when the treated surface is exposed.

Cleaning

石墨烯玻璃鳞片底漆 DreamCover 152 Gns Painting and paint film drying process should keep the surrounding air clean, and should not be painted in a dust environment.

4. 石墨烯玻璃鳞片底漆 Graphite glass flake primerPaint deployment

石墨烯玻璃鳞片底漆 DreamCover 152 GnsPaint shall be prepared strictly according to the product instructions of the paint manufacturer.

The strictly check the should be of inspected, unqualified and expired石墨烯玻璃鳞片底漆 DreamCover 152 GnsPainting shall not be used for painting. Before use, the paint must be mixed and fully mixed according to the regulations to make it fully mixed.

In layered coating, the color of each layer shall be maintained with enough contrast to check whether the surface is completely covered.

5. 石墨烯玻璃鳞片底漆 Graphite glass flake primerPainting and brush method

石墨烯玻璃鳞片底漆 DreamCover 152 GnsHigh pressure without air spraying method, brush coating or compressed air spraying construction method can also be used.

Brush coating

Brush coating石墨烯玻璃鳞片底漆 DreamCover 152 Gns, make paint brush dip in have right amount of coating, distribution is in quite be coated inside the surface range, be extended horizontally first, then longitudinal straighten out, make coating distribution evenly. Can also be the first vertical extension, and then horizontal rationalization, step by step, do not omit.

Compressed air spraying:

Compressed air spraying is the use of compressed air to attract (or compress) the coating from the pot to the spray gun. At 0.2 ~ 0.5 Mpa, the coating mixes the air with the spray and sprays on the coated surface to get an evenly distributed coating.

Airless spraying

High pressure airless spraying usually uses compressed air operation to drive the high pressure pump, the paint is inhaled and pressurized to 10 ~ 25 Mpa, through the high pressure hose and spray gun, and finally through the olive-shaped nozzle. When the paint leaves the nozzle, the atomization into very fine particles, sprayed to the coated surface, forming a uniform film.

6.Other requirements

In order to ensure the thickness of the film of welds, edges, edges and corners, a large area of gas spraying 石墨烯玻璃鳞片底漆 DreamCover 152 Gnsbefore,preit with a brush.

石墨烯玻璃鳞片底漆 DreamCover 152 GnsDuring pneumatic spraying, the operator shall measure the wet film thickness gauge at any time to control石墨烯玻璃鳞片底漆 DreamCover 152 Gnspaint film thickness,if manually painted, the number of coating channels should be increased accordingly to ensure that the specified thickness of paint film.

Application石墨烯玻璃鳞片底漆 DreamCover 152 Gnsshould use the first up and down after the left and right, or the first left and down after the vertical and horizontal spraying method, so that the paint film smooth and smooth, uniform thickness.

Paint shall be done with brushes of the right specification, except for use of painting equipment or drum.

When spraying equipment is used, the painting equipment shall always be precise and fully controlled to prevent damage to adjacent surfaces. When spraying with the spray gun, the operation rules of the spray gun must be strictly observed, and the spray gun shall not be painted outdoors in rain, snow, fog and windy days.

7.Welcome to order the石墨烯玻璃鳞片底漆 DreamCover 152 Gns

We expect that in the future development process, products and services will be recognized by everyone, at the same time, establish a good Corporate Culture and social responsibility, create excellent value for employees and customers, for the society and environment. In the future, we will always stay true to our original aspiration, forge ahead, continue to focus on the field of industrial anticorrosion, and strive to become a "trustworthy partner" in the eyes of customers. Protect your assets and enhance the value of your products through our professional and diversified services.

"Graphene glass flake paint is a two-component high solid epoxy paint composed of graphene, epoxy resin, glass flake pigments and amine curing agents. Graphene glass flake paint is suitable for severe corrosive environments and withstands wear and tear Steel and concrete protection in various environments. Such as offshore structure submerged areas, tidal range areas and splash areas, as well as docks, hydraulic gates, underground pipelines, etc. It can also be used for anti-corrosion coatings on the inner walls of liquid tanks and storage tanks."