1. About 无机富锌底漆 Inorganic Zinc-rich primerthe adhesion force

DreamZinc 88: This product is a two component self drying coating composed of advanced inorganic silicone resin, zinc powder, additives, and solvents as the second component, and an inorganic curing agent as the other component. Rich in zinc powder, the electrochemical protection effect of zinc powder; High hardness of paint film; High temperature resistance, without affecting welding performance; Excellent drying performance; High adhesion and good mechanical properties.

DreamZinc 88Adhesion is the firmness of the paint layer and the surface of the painted object through the action of physical or chemical forces.DreamZinc 88Coating adhesion is the most important indicator for evaluating a coating or coating system. Is the premise of paint film with a series of properties.DreamZinc 88The methods of adhesion test include: drawing circle method, drawing method, drawing method, twist method and ASTM, etc

2. The role of the adhesion force

1) Good adhesion can effectively block theDreamZinc 88penetration of the external electrolyte solution into the matrix, and delay the formation of interfacial corrosion;

2) Strong interface adhesion can greatly prevent the diffusion of corrosion products-metal cations to the cathode area through the side of the phase;

3. Pull method (pull method)

Basis: color paint and varnish, pull open method adhesion test GB / T5210-2006, this method is more professional, need professional instrument: pull instrument

3.1. Pull steps

A. Instruments and equipment: the prepared sample (according to the design requirements, film thickness)

B. Testing instrument: sandpaper, transparent tape, cutting tool, aluminum alloy cylinder mold, adhesive, drawing instrument.

c. method of operation:

1) Aluminum alloy column with 240-400 mesh fine sandpaper sand, before use with solvent scrub to remove oil;

2) Solremoval shall be used at the test site;

3) Apply the adhesive to the aluminum alloy cylinder, press it on the surface of the test coating, and turn to 360 to ensure that all parts are attached with the adhesive;

4) The aluminum alloy cylinder is fixed on the coating surface with tape, and the adhesive should solidify for 3 hours at room temperature (subject to the weather temperature and environmental humidity on the day of the experiment);

5) Before the test, use the aluminum alloy cylinder to cut the coating material;

6) Cover the aluminum alloy cylinder with the tension instrument, turn the handle for testing, record the damage strength (MPa), and the damage state. Show the adhesion strength and state of the coating and the adhesion between the substrate, the coating, the coating and the glue, and the glue and the cylinder;

3.2. Description method of drawing the coating fault state:

A: Incohesive destruction of substrate

A: Incohesive destruction of substrate

B: Coin failure of the first paint

B / C: the interlayer adhesion damage of the first and second paint

C: cohesin failure of the second paint

C / D: the interlayer adhesion damage of the second and third paint

D: cohesin failure of the third paint

D / Y: interlayer adhesion between the last coating and glue

Y: the cohesive destruction of the glue

Y / Z: interlayer adhesion between glue and test rod

Z: Inin destruction of test rod

The strength of adhesion is expressed as N/mm2 (Mpa), which is shown on the common Elcometer 108.

The following figure is an example:

For example,DreamZinc 88if the tensile stress of a coating system is 13.17MPa, the first coating has 45% of the coating cohesion damage, and the last layer adhesion between the coating and the glue reaches 50% of the cylinder area, it can be described as: 13.17MPa, 45%D 55%D / Y.

4. Welcome to orderDreamZinc 88

We expect that in the future development process, products and services will be recognized by everyone, at the same time, establish a good Corporate Culture and social responsibility, create excellent value for employees and customers, for the society, the environment. In the future, we will always stay true to our original aspiration, forge ahead, continue to focus on the field of industrial anticorrosion, and strive to become a "trustworthy partner" in the eyes of customers. Protect your assets and enhance the value of your products through our professional and diversified services.

Inorganic zinc-rich primer is a two-component solvent-based self-curing inorganic zinc-rich primer; it complies with the requirements of type Ⅰ and category 2 in HG/T3668. The metallic zinc content of the dry film is ≥70%. Performance characteristics: Excellent cathodic protection and anti-rust effect; excellent anti-corrosion, weather resistance and wear resistance; long-term temperature resistance up to 400°C in dry environment; excellent resistance in media with pH value of 6-9 Chemically resistant; a solderable primer. Used in containers, storage tanks, offshore drilling platforms, steel structures, ships and other places.